ANALYSIS OF CHANGES IN THE STRUCTURE FORMATIONOF ZINC-BASED INTERMETALLIC LAYERS DURING GALVANIZINGOF HEAT-HARDENED STEEL PRODUCTS BY DIFFUSION METHODFROM THE GAS PHASE

Authors

  • I. A. Buloichyk Belorussian National Technical University, 65 Nezavisimosti Ave., 220013 Minsk, the Republic of Belarus Автор

Keywords:

thermodiffusion galvanizing in powder saturating media; corrosion protection; diffusion layer; microstructure; microhardness

Abstract

Data on the study of the formation of zinc intermetallic diffusion layers on thermally hardened surfaces under conditions of structural change of the metal are presented. For zinc diffusion layers formed on a martensitic steel base, an increase in the values of microhardness and the zone of formation of a solid solution of zinc in iron (α-phase) was observed in comparison with zinc diffusion layers formed on steel with a pearlite structure.

Fig. 5. Ref.: 5 titles.

Downloads

Published

2021-11-01

Issue

Выпуск 10. 2021 год

Section

МАШИНОСТРОЕНИЕ И МАШИНОВЕДЕНИЕ

License

Copyright (c) 2023 Вестник БарГУ Серия "Технические науки"

Лицензия Creative Commons

Это произведение доступно по лицензии Creative Commons «Attribution-NonCommercial» («Атрибуция — Некоммерческое использование») 4.0 Всемирная.

Авторы сохраняют за собой право заключать определенные договорные соглашения, касающиеся неисключительного распространения опубликованной версии работы (например, размещать ее в институциональном репозитории, публикация в книге) со ссылкой на ее первоначальную публикацию в этом журнале.